Diamond ASA S225 LG
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7EbF5R_Diamond-ASA-S225-LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond ASA S225 LG is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 3.18 mm, Injection Molded) | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18 mm, Injection Molded | 42.7 | MPa | |
| Break, 23°C, 3.18 mm, Injection Molded | 37.9 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 23°C, 3.18 mm, Injection Molded | 3.2 | % | |
| Break, 23°C, 3.18 mm, Injection Molded | 42 | % | |
| Flexural Modulus - Tangent 3(23°C, 3.18 mm, Injection Molded) | 2030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 81 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm, Injection Molded) | 77.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 235 to 260 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Method I (3 point load), 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6060 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Vyncolit® 1914 | Vyncolit N.V. | Epoxy | Vyncolit® |
| ADDILENE H 210 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Cri-Line LC-612-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Hylon® N1025THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |