POCAN® DP 7318 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7CH8EH_POCAN-DP-7318-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 17 % white pigments, injection molding, improved light reflection, low tendency to warp |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.50 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 27.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 3.00 mm 1 | 1.9 | % | |
| Across Flow : 110°C, 1 hr, 3.00 mm 2 | 0.20 | % | |
| Flow : 260°C, 3.00 mm 3 | 1.9 | % | |
| Flow : 110°C, 1 hr, 3.00 mm 4 | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (Reduced Viscosity) | 94.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 57.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 10 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 3200 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 95.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHMR, 09-030, MD17 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 130 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 110 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 600 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 600 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 1050 | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| AVALON® 55 AEX | Huntsman Corporation | TPU-Polyester | AVALON® |
| Crastin® SK645FR NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Daelim Po1y® LD-18AS | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| Grilamid® L 25 W 20 X | EMS-GRIVORY | Nylon 12 | Grilamid® |