ASTAGLAS™ DR101
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAGLAS™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Bvgex_ASTAGLAS-DR101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAGLAS™ DR101 is a transparent high impact and heat resistance Poly(Methyl Methacrylate) Acrylic for injection moulding and extrusion processes. Typical applications require an optimum balance of toughness and heat resistance products for automotive, lighting, appliance and houseware applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.55 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 45 | ||
| R-Scale | 110 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2000 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 42.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 35 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 1820 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 46 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 6(1.8 MPa, Annealed, 3.20 mm) | 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 7 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (Total, 3200 µm) | 90.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 210 to 240 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 85.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 40 to 80 | rpm | |
| Clamp Tonnage | 5.0 to 9.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Annealed 4 hr at 80°C |
| 7 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7868-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Next Nylon 6 Prime Series NG15-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| DURANEX® 303RA | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Axiall PVC 7255 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Vydyne® 65B | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |