Celstran® PA66-GF40-02-Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Bg6Kz_Celstran-PA66-GF40-02-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Long glass fiber reinforced, heat stabilized, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow | 0.20 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 14500 | MPa | ASTM D638 |
| 23°C | 14200 | MPa | ASTM D638 |
| 121°C | 7310 | MPa | ASTM D638 |
| -- | 13300 | MPa | ISO 527-2/1A/1 |
| 80°C | 7500 | MPa | ISO 527-2/1A |
| Tensile Strength | |||
| Fracture, -40°C | 270 | MPa | ASTM D638 |
| Fracture, 23°C | 253 | MPa | ASTM D638 |
| Fracture, 121°C | 134 | MPa | ASTM D638 |
| Fracture | 215 | MPa | ISO 527-2/1A/5 |
| 80°C | 120 | MPa | ISO 527-2/1A |
| Tensile Elongation | |||
| Fracture, -40°C | 2.2 | % | ASTM D638 |
| Fracture, 23°C | 2.3 | % | ASTM D638 |
| Fracture, 121°C | 2.5 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/1A/5 |
| Fracture, 80°C | 2.9 | % | ISO 527-2/1A |
| Flexural Modulus | ISO 178 | ||
| 23°C | 13500 | MPa | ISO 178 |
| 80°C | 6800 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 355 | MPa | ISO 178 |
| 80°C | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 26 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 46 | kJ/m² | ISO 179/1eU |
| 23°C | 95 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 43 | kJ/m² | ISO 180/1U |
| 23°C | 47 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy (-30°C) | 17.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 254 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 255 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 240 | °C | ISO 75-2/C |
| Melting Temperature 1 | 261 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Nozzle Temperature | 300 - 315 | °C | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 300 to 315°CFeed Temperature: 20 to 50°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GF 25 1 L black (4637) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Evoprene™ GC 5699 | AlphaGary | SEBS | Evoprene™ GC |
| LUVOCOM® 3-7281/PL/HI/BK | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |
| PETOPLEN EH 341 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |
| CYCOLOY™ CX7240U resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |