Hytrel® HTR8139BK
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7BO9sY_Hytrel-HTR8139BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 44 Shore D, Lubricated, High Viscosity Polyester Elastomer Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.90 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.4 | % | |
| Flow | 1.6 | % | |
| Water Absorption | |||
| 24 hr | 0.70 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 44 | ||
| Shore D, 15 sec | 40 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 55.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 32.0 | MPa | |
| 5.0% Strain | 4.50 | MPa | |
| 10% Strain | 6.70 | MPa | |
| 50% Strain | 11.8 | MPa | |
| 100% Strain | 14.0 | MPa | |
| 300% Strain | 23.0 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 510 | % | ISO 527-2 |
| Flexural Modulus | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 58.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 44.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -100 | °C | ISO 974 |
| Glass Transition Temperature 1 | -45.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 194 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-4 | cm/cm/°C | |
| Transverse | 1.9E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.90 | ||
| 1 MHz | 4.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.0E-3 | ||
| 1 MHz | 0.028 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 21 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 0.960 | g/cm³ |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2211 HF | RTP Company | PEEK | RTP |
| Spartech Polycom SC7-7022UR | Spartech Polycom | PC | Spartech |
| LEXAN™ FXD104R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| MACOMASS PP MM-PP BI 81 Copolymer | MACOMASS Verkaufs AG | PP Copolymer | MACOMASS PP |
| Sylvin 29000-60 Clear Yellow 4218 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |