TEKAMID™ TA250G15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7B0ynu_TEKAMID-TA250G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TEKAMID™ TA250G15 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 118 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5490 | MPa | ASTM D790 |
| Flexural Strength | 196 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 42 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 240 | °C | |
| 1.8 MPa, Unannealed | 225 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D2133 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-315 (Roto) | Ravago Manufacturing Americas, LLC | HDPE | Ravago Compounds |
| Karina RED COLOR CONCNETRATE 42/155-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lumid® HI1202A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| POLYFLON™ M-12 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| OTECH PVC OW749 - Riser Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |