Exelene® LDPE 2501

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Montachem International, Inc.
Trademark:	Exelene® LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7AcU2R_Exelene-LDPE-2501.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Applications:

0,5 - 1,0 kg bags for packing powdered foods and grains such as rice, pulses, salt, sugar and flour

High clarity and shinny bags for packing solid foods such as bread, tarts, vegetables and fruits

Bags for packing personal and domestic products such as gloves, silverwear, drinking glases and napkins

Characteristics:

The Exelene resin LDPE 2501 meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antiblock Antioxidant Slip
Features	Antiblocking Antioxidant Food Contact Acceptable High Clarity Low Density Slip
Uses	Bags Food Packaging Food Service Applications Non-specific Food Applications
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Blown Film Film Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.921	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.5	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Flexural Strength ¹			ASTM D882
-- ²	190	MPa
-- ³	172	MPa

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	38	µm
Tensile Strength ⁴			ASTM D882A
MD : Break	21.0	MPa
TD : Break	17.9	MPa
Tensile Elongation ⁵			ASTM D882A
MD : Break	260	%
TD : Break	540	%
Dart Drop Impact ⁶(38000 µm)	110	g	ASTM D1709A

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	111	°C	DSC

Optical	Nominal Value	Unit	Test Method
Haze	5.0	%	ASTM D1003

Note Message
1 .	5.1 mm/min
2 .	TD, 1% secant
3 .	MD, 1% secant
4 .	510 mm/min
5 .	510 mm/min
6 .	F50, 66 cm

Resin Grade	Manufacturer	Category	Trademark
Resinoid 1371	Resinoid Engineering Corporation	Phenolic	Resinoid
Nipol® LX426	Zeon Corporation	Latex	Nipol®
Exxtral™ Performance Polyolefin HMU208	ExxonMobil Chemical	TPO	Exxtral™ Performance Polyolefin
Gallonprene® GP520-9002	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Karina IVORY PVC COMPOUND 105900-35/1 1-B-ACE	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina