Celazole® (T Series) TF-60V
| Category: | PBI , Polybenzimidazole |
| Manufacturer: | PBI Performance Products, Inc. |
| Trademark: | Celazole® (T Series) |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 791aIh_Celazole-T-Series-TF-60V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celazole TF-60V is a glass-reinforced blend offering thermal and electrical insulation, wear resistance and dimensional stability with the cost efficiency of a direct form process. An excellent choice for high temperature electrical insulators, plasma torch drag cup shields, swirl baffles and parts requiring minimal thermal expansion. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.25 | % | |
| Equilibrium | 4.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (A-Scale) | 30 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12100 | MPa | ASTM D638 |
| Tensile Strength | 152 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.4 | % | ASTM D638 |
| Flexural Modulus | 12500 | MPa | ASTM D790 |
| Flexural Strength | 225 | MPa | ASTM D790 |
| Compressive Modulus | 3650 | MPa | ASTM D695 |
| Compressive Strength | 221 | MPa | ASTM D695 |
| Poisson's Ratio | 0.34 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 310 | °C | ASTM D648 |
| CLTE - Flow (24 to 149°C) | 1.6E-5 | cm/cm/°C | TMA |
| Thermal Conductivity (24°C) | 0.36 | W/m/K | ASTM F433 |
| Heat Capacity (70°C) | 1130 | J/kg/°C | DSC |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature of Intial Weight Loss | Internal Method | ||
| Air | 607 | °C | |
| Nitrogen | 635 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.90 | ||
| 10 kHz | 3.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.0 | ||
| 10 kHz | 1.0E-3 | ||
| Arc Resistance | 180 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1718-PUV | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Taitacell EPS 321S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Vi-Chem PVC VNC85-80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TRANSMARE® 19HT20-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| LNP™ STAT-LOY™ PF303 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ STAT-LOY™ |