LNP™ STAT-KON™ DE0029E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 78YHLu_LNP-STAT-KON-DE0029E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DE0029E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. Flame Retardant, Electrically Conductive. Also known as: LNP* STAT-KON* Compound DC-1002 EM FR PB Product reorder name: DE0029E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.29 to 0.43 | % | ISO 294-4 |
| Flow : 24 hr | 0.060 to 0.32 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 7800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 110 | MPa | ASTM D638 |
| Break | 117 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.5 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 8650 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 183 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 61 | J/m | ASTM D256 |
| 23°C 2 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 17.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 139 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 FI | Nilit Plastics | Nylon 66 | POLYNIL® |
| Multiuse Leostomer® LJ-3160N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| DINALON® A1S25 DI H | Grupo Repol | Nylon 66 | DINALON® |
| DynaPath™ 4155-C | Polymer Dynamix | PPA | DynaPath™ |
| Techsil® RTV12120 | Techsil Limited | Silicone Rubber, RTV-1 | Techsil® |