VESTAMID® D DX9302
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® D |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 78LHTP_VESTAMID-D-DX9302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characterization: elastomer modified, heat-stabilized Applications: low-extract windshield wiper lines, corrugated pipes Its advantages over PA 12 exhibit in the
The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.02 | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1150 | 850 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 30.0 | 26.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 15 | 23 | % | |
| Break | > 50 | > 50 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C, Complete Break | 19 | -- | kJ/m² | |
| -30°C, Partial Break | -- | 17 | kJ/m² | |
| 23°C, Partial Break | 90 | 100 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 140 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | 110 | °C | ISO 306/B |
| Melting Temperature 2 | 215 | 215 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.7E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 41 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.80 | -- | ||
| 1 MHz | 3.00 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.047 | -- | ||
| 1 MHz | 0.037 | -- | ||
| Comparative Tracking Index 3(Solution A) | > 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Electrolytical Corrosion | AN 1,2 | -- | IEC 60426 | |
| ISO Shortname | PA612-HI, EH, xx-010 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
| 2 . | 2nd Heating |
| 3 . | 50 drops Value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ MH-82 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Kepital® ET-20H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| OmniLon™ PA6 GR43 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |
| OPNYL OP66UT 119 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| ROTOLENE® Industrial | Polimeros Mexicanos S.A. de C.V. | LMDPE | ROTOLENE® |