Optix® CP-924
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Plaskolite West, Inc. |
| Trademark: | Optix® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 77v9qN_Optix-CP-924.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Optix®CP-924 is a polymethyl methacrylate-acrylic acid product,. It can be processed by injection molding and is available in North America or Europe. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.4 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 68 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 58.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Flexural Strength | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact | 480 | J/m | ASTM D256 |
| Dart Drop Impact | 1.58 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 87.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| CLTE - Flow (-30 to 30°C) | 7.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 91.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Thermal Index, UL-746 ABC: 50°CBurn Rate, ASTM D635: 1.6 in/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 73.9 | °C | |
| Rear Temperature | 204 - 249 | °C | |
| Middle Temperature | 210 - 254 | °C | |
| Front Temperature | 216 - 260 | °C | |
| Nozzle Temperature | 210 - 260 | °C | |
| Processing (Melt) Temp | 210 - 249 | °C | |
| Mold Temperature | 48.9 - 79.4 | °C |
| Injection instructions |
|---|
| Heated Manifold: 410-480°FHeated Drop (Sprue): 410-480°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® F284 | Solvay Specialty Polymers | PTFE | Polymist® |
| Tecomid® NA40 GR14 NL MC | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Vi-Chem PVC PNC87-5-8135 | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Rotuba CAB B900 (20% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| XYLEX™ X8210 resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |