TECHNYL® C 218 V35 BLACK 21N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 76e9Ar_TECHNYLC218V35BLACK21N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 218 V35 Black 21N is a polyamide 6, reinforced with 35% of glass fiber, heat stabilized, for injection moulding. The product offers an excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183/A |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Saturated, 23°C | 2.1 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | 6500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 195 | 115 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 3.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 9600 | -- | MPa | ASTM D790 |
| 23°C | 9600 | 6000 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 260 | -- | MPa | ASTM D790 |
| 23°C | 280 | 185 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ||||
| 23°C | 83 | 94 | kJ/m² | ISO 179/1eU |
| 23°C | 74 | 80 | kJ/m² | ISO 179/1fU |
| Notched Izod Impact (23°C) | 15 | 28 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, not annealed | 205 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | -- | 22 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.6 mm | 650 | -- | °C | IEC 60695-2-12 |
| 3.2 mm | 650 | -- | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin UVFT3082-74 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sinvicomp SSG7006 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| CALP 4700G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Chemical Resources PMMA1100 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| Novalloy-S S1220 | PlastxWorld Inc. | PC+ABS | Novalloy-S |