ACRYPET® IR G504
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon Co., Ltd. |
| Trademark: | ACRYPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 76aKZD_ACRYPET-IR-G504.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Acrypet®IR G504 is a polymethyl methacrylate-acrylic material,. This product is available in North America,. Acrypet®The main characteristics of IR G504 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.90 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 64 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 44.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 85 | % | ASTM D638 |
| Flexural Modulus (6.35 mm) | 1770 | MPa | ASTM D790 |
| Flexural Strength (6.35 mm) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 58 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 89.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| CLTE - Flow | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Surface Resistivity, JIS K6911: >10^16 ohmVolume Resistivity, JIS K6911: >10^15 ohm-cmDielectric Breakdown Strength: 15 kV/mmDielectric Constant, 60Hz: 3.8Dielectric Loss Tangent, 60Hz: 0.04Arc Resistance, JIS K6911: No Trace |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 682 HB | RTP Company | ABS | RTP |
| MOSTEN NB 220 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Veroplas VF790 | PlastxWorld Inc. | ABS | Veroplas |
| Karina BLACK PVC COMPOUND 75930-48/ 1-F-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ XHT1141 resin | SABIC Innovative Plastics | PC | LEXAN™ |