Styrolution PS 6200/6201
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 76Cgtu_Styrolution-PS-6200-6201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styrolution PS 6200/6201 is a High Impact Polystyrene product. It can be processed by extrusion, injection molding, or thermoforming and is available in Latin America or North America. Applications of Styrolution PS 6200/6201 include containers, decorative parts, food contact applications, kitchenware and medical/healthcare. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | |||
| -- 1 | 0.59 to 0.64 | g/cm³ | |
| -- 2 | 0.62 to 0.67 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.1 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2140 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 24.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 49.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 83.9 | °C | |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 3 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.18 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1.00 mm, 1 MHz) | 2.50 | ASTM D150 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 60 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 182 to 277 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | without external lubricant |
| 2 . | with external lubricant |
| 3 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F500EP (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Leona™ FG173 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Plenco 03356 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| ADVANCENE™ EM-2420-AAB | ETHYDCO | LLDPE | ADVANCENE™ |
| TAFMER™ BL2481M | Mitsui Chemicals, Inc. | PAO | TAFMER™ |