Generic Acetal (POM) Copolymer - Carbon Fiber
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 75yHyS_Generic-Acetal-POM-Copolymer---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 - 1.58 | g/cm³ | ASTM D792 |
| 23°C | 1.42 - 1.50 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 - 19 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.00 - 2.45 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.73 | % | ASTM D955 |
| 23°C | 0.35 - 1.2 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.19 - 0.26 | % | ASTM D570 |
| 23°C, 24 hr | 0.10 - 0.11 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 7390 - 17500 | MPa | ASTM D638 |
| 23°C | 6970 - 17300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 55.0 - 148 | MPa | ASTM D638 |
| Yield, 23°C | 51.0 - 140 | MPa | ISO 527-2 |
| Fracture, 23°C | 62.3 - 121 | MPa | ASTM D638 |
| Fracture, 23°C | 68.8 - 170 | MPa | ISO 527-2 |
| 23°C | 66.2 - 133 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.4 - 2.8 | % | ASTM D638 |
| Yield, 23°C | 0.70 - 3.1 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 2.6 | % | ASTM D638 |
| Fracture, 23°C | 0.80 - 4.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6470 - 13800 | MPa | ASTM D790 |
| 23°C | 5750 - 16200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 95.2 - 237 | MPa | ASTM D790 |
| 23°C | 57.5 - 210 | MPa | ISO 178 |
| Coefficient of Friction | 0.11 - 0.37 | ASTM D1894 | |
| Wear Factor | 5.0 - 10000 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 5.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 14 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 32 - 70 | J/m | ASTM D256 |
| 23°C | 3.7 - 5.1 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 130 - 540 | J/m | ASTM D256 |
| 23°C | 15 - 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 - 166 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 133 - 163 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 153 - 163 | °C | ISO 75-2/A |
| Continuous Use Temperature | 99.6 - 100 | °C | ASTM D794 |
| Vicat Softening Temperature | 160 - 165 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 1.5E-6 - 6.3E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.8E-5 - 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.7E-5 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 1.3E+12 | ohms | ASTM D257 |
| -- | 10 - 2.5E+9 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0 - 1.3E+5 | ohms·cm | ASTM D257 |
| 23°C | 30 - 2.5E+5 | ohms·cm | IEC 60093 |
| Insulation Resistance (23°C) | 10 - 2.5E+9 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.9 - 121 | °C | |
| Drying Time | 1.9 - 5.0 | hr | |
| Rear Temperature | 182 - 183 | °C | |
| Middle Temperature | 195 - 199 | °C | |
| Front Temperature | 190 - 216 | °C | |
| Nozzle Temperature | 188 | °C | |
| Processing (Melt) Temp | 200 - 201 | °C | |
| Mold Temperature | 93.1 - 100 | °C | |
| Injection Pressure | 85.8 - 86.4 | MPa | |
| Back Pressure | 0.250 - 0.568 | MPa | |
| Screw Speed | 45 - 47 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMAPET® H1 | Indorama Ventures PCL | PET | RAMAPET® |
| Mirathane™ E295U | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Tianchen J-700 | Shandong Tianchen Chemical Co., Ltd | CPVC | Tianchen |
| ALCUDIA® HDPE 5502-A | REPSOL | HDPE | ALCUDIA® HDPE |
| Enviramid® N2320HL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |