Mecoline I RDX 5210 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 75P5mz_Mecoline-I-RDX-5210-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A high performance radiation cross-linkable compound, offering excellent mechanical and electrical properties |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 54 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 1 | 20.0 | MPa | |
| -- 2 | > 10.0 | MPa | |
| Tensile Strain | IEC 811-1-1 | ||
| Break 3 | 250 | % | |
| Break 4 | > 600 | % | |
| Abrasion | 190 | cm | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5 | 70.1 | kN/m | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 190 to 200 | °C | |
| Extruder Screw L/D Ratio | >24.0:1.0 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | Internal Method | ||
| 150°C, 3000 hr | 15 | % | |
| 180°C, 240 hr | 5.0 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 to 170 | °C | |
| Cylinder Zone 2 Temp. | 180 to 190 | °C | |
| Cylinder Zone 3 Temp. | 190 to 200 | °C | |
| Cylinder Zone 4 Temp. | 190 to 200 | °C | |
| Cylinder Zone 5 Temp. | 190 to 200 | °C | |
| Adapter Temperature | 190 to 200 | °C | |
| Die Temperature | 205 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | After crosslinking |
| 2 . | Before crosslinking |
| 3 . | After crosslinking |
| 4 . | Before crosslinking |
| 5 . | After crosslinking |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYpropen PPC 12000 | Polykemi AB | PP Copolymer | POLYpropen |
| Sinvicomp SSZ6061 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Moplen EP1X35F | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Moplen |
| Celanex® XFR 4840 | Celanese Corporation | PBT | Celanex® |
| Cheng Yu T885GV3 | Cheng Yu Plastic Company Limited | PBT | Cheng Yu |