Sumikon® PM-5630
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 75GQ56_SumikonPM5630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON PM-5630 Type Black is a Mineral & Short Glass fiber molding compound based on Phenolic Resol polymer. It is supplied in the form of Granular/Molding Powder for Molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.18 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.25 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.11 | % | JIS K6911 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 97.0 | MPa | JIS K6911 |
| Flexural Modulus | 20100 | MPa | JIS K6911 |
| Flexural Strength | 149 | MPa | JIS K6911 |
| Compressive Strength | 282 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.1 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 300 | °C | JIS K6911 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T-27 GF 35 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Nypol® PA A3 HF NTLA010 NR430 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| CERTENE™ LLGF-123D | Muehlstein | LLDPE | CERTENE™ |
| LightSpan® LS2-6140 | NuSil Technology | Silicone | LightSpan® |
| LNP™ LUBRICOMP™ CX05031 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ LUBRICOMP™ |