Akulon® Diablo HT-HG0 (K-X07029)
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 74wZt3_Akulon-Diablo-HT-HG0-K-X07029-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® Diablo HT-HG0 (K-X07029) is a Polyamide 66/6 Copolymer (Nylon 66/6) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Akulon® Diablo HT-HG0 (K-X07029): Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.58 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.56 | -- | % | |
| Flow | 0.37 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 230 | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | 4.6 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 90 | kJ/m² | |
| 23°C | 95 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 275 to 295 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 108950 E | RTP Company | Nylon 6 | RTP |
| Unichem 7011C2-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Evoprene™ COGEE 682 | AlphaGary | SEBS | Evoprene™ COGEE |
| LNP™ THERMOCOMP™ UX06032-WH9E041 compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |
| SQUARE® LSR8620-35A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |