Latamid 66 H2 G/35-V0HF1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 74oA3T_Latamid-66-H2-G-35-V0HF1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 (PA66) based compound. Heat stabilised. Glass fibres. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 1.0 | % | |
| Flow : 2.00 mm | 0.35 to 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 245 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 775 | °C | |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2307FB | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Vital-Line SHM3905 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Carbotex K-30FRT12 | Kotec Corporation | PC | Carbotex |
| Clariant Nylon 6/6 66G43M | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Impet® 830R | Celanese Corporation | PET | Impet® |