LNP™ THERMOCOMP™ NF004 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 74G7Bs_LNP-THERMOCOMP-NF004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP NF004 is a compound based on PC+ABS resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PCA-F-1004 Product reorder name: NF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.58 | % | ISO 294-4 |
| Flow : 24 hr | 0.41 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6890 | MPa | ASTM D638 |
| -- | 6480 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 97.2 | MPa | ASTM D638 |
| Break | 95.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.5 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6210 | MPa | ASTM D790 |
| -- | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 138 | MPa | ASTM D790 |
| -- | 143 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.2 | J | ASTM D3763 |
| -- | 5.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 134 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® GF8001 | Covestro - Polycarbonates | PC | Makrolon® |
| Infino LF-1025 | SAMSUNG SDI CO., LTD. | PC | Infino |
| Lucent PC PC-1403FD | Lucent Polymers, Inc. | PC | Lucent PC |
| LOTTMER HX-064AB | Lotte Chemical Corporation | TPE | LOTTMER |
| TAFMER™ DF940 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |