SCHULABLEND® (PA/PP) M/MO 5101
| Category: | Nylon+PP , Polyamide + PP |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 73a4y3_SCHULABLENDPAPPMMO5101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6/PP blend with excellent chemical resistance |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.01 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 11.0 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1800 | 1100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | 38.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.0 | 21 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 49 | -- | kJ/m² | ISO 179/1eU |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 119 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 202 | -- | °C | ISO 306/A50 |
| -- | 120 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.6 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PPE-LXS314-20 | Polymer Technology and Services, LLC | PPE+PS | PTS |
| Sinpolene MBW3422 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Badaflex® TPE-S 60A 1017 | Bada AG | SEBS | Badaflex® |
| Huafon EP127 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| Kuraray Poval® PVA 403 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |