Radilon® A ERV1906LK 100 NAT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 73TS6v_Radilon-A-ERV1906LK-100-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 13% glass fiber reinforced injection moulding grade. Toughened, lubricated and heat stabilized. Natural colour. Suitable for parts requiring improved impact strength along with enhanced stiffness. A typical application are anti-vibration rings. ISO 1043 : PA66-IT GF13 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.22 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 7.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5000 | 4200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | |||
| Yield | -- | 75.0 | MPa | |
| Break | 100 | -- | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | |||
| Yield | -- | 8.0 | % | |
| Break | 4.0 | -- | % | |
| Nominal Tensile Strain at Break | -- | 17 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 4300 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 150 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.8 | 5.0 | kJ/m² | |
| 23°C | 12 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 42 | kJ/m² | |
| 23°C | 75 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 230 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 175 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 235 | -- | °C | ISO 306/B50 |
| Melting Temperature | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 10 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1603 | RTP Company | PAS | RTP |
| Telcar® GSE5573 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Sylvin 5134-76 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CP PRYME® Polypropylene PPH100-12M | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |
| Dryflex® 662750S | ELASTO | SEBS | Dryflex® |