RELENE® 1070LA17
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 73Mgyu_RELENE-1070LA17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 1070LA17 is an extrusion coating grade Low Density Polyethylene (LDPE) produced by high pressure autoclave process. This grade is specially developed for extrusion coating on different substrates and contains no additives. It exhibits excellent drawdown characteristics maintaining good adhesion, with very low neck-in even at high line speeds. It can also be easily processed into thin gauge films for adhesive lamination and heat pressure lamination. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 18.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 15.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 250 | % | |
| TD : Break, 40 µm, Blown Film | 400 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® SX01 | Toray Resin Company | Nylon 6+ABS | Toyolac® |
| GAPEX® RPP25DZ02NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Elastron® G G103.A70.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina CLEAR CRYSTAL PVC COMPOUND -E 70/200-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® Nylon 627L | The Plastics Group | Nylon 66 | Polifil® Nylon |