MAJORIS DW254
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 722NIy_MAJORIS-DW254.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DW254 is a 25% glass fiber/mineral polypropylene compound intended for injection moulding. The product is available in both natural (DW254) and black (DW254-8229) but other colours can be provided on request. DW254 has been developed especially for the furnitures, sport, leisures applications . This product is antistatic and UV stabilised. DW254 makes it very easy to process even for complicated parts with long flow paths and it offers very high productivity with short cycle times. DW254 is formulated to give an excellent surface finish. APPLICATION Products requiring good rigidity, low shrinkage, high dimensional stability can suitably be made from DW254. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 52 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure. |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 1954 | Covestro - Polycarbonates | PC | Makrolon® |
| AZDEL™ U421B02N (Longitudinal) | Azdel, Inc. | PP Alloy | AZDEL™ |
| ALCOM® PS 500/2.2 C20-EMPERA116 | ALBIS PLASTIC GmbH | PS (GPPS) | ALCOM® PS |
| PEXTIN™ PET 545 BK | Pier One Polymers, Inc. | PET | PEXTIN™ |
| Plaskon SMT-B-2 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |