XENOY™ X2500UV resin
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 71nDi8_XENOY-X2500UV-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XENOY X2500UV is a medium viscosity, unfilled, UV stabilized, elastomer modified PC/PET blend with excellent heat and impact performance. ISO1043-label: PC+PET-I. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/1.2 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.80 | % | |
| Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Across Flow 2 | 0.50 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.70 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2200 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.0 | MPa | ASTM D638 |
| Yield 4 | 56.0 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/50 |
| Break 5 | 55.0 | MPa | ASTM D638 |
| Break | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield | 5.0 | % | ASTM D638, ISO 527-2/50 |
| Yield 6 | 5.0 | % | ASTM D638 |
| Break | 100 | % | ASTM D638 |
| Break 7 | 80 | % | ASTM D638 |
| Break | 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 2150 | MPa | ASTM D790 |
| -- | 2100 | MPa | ASTM D790 |
| -- 9 | 2150 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 79.0 | MPa | ASTM D790 |
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 79.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11 | ISO 179/1eA | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength 12(-30°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 200 | J/m | ASTM D256 |
| 0°C | 450 | J/m | ASTM D256 |
| 23°C | 600 | J/m | ASTM D256 |
| -40°C 13 | 15 | kJ/m² | ISO 180/1A |
| -30°C 14 | 25 | kJ/m² | ISO 180/1A |
| 23°C 15 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 16(-30°C) | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 17 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 18 | 108 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525, ISO 306/B50 12 19 |
| -- | 145 | °C | ISO 306/A50 |
| -- | 136 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 8.7E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.18 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | ||
| 60 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index (2.70 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 250 to 275 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 265 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | Type I, 50 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2404AF00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| NEXT SIGNATURE PPH T40-100 | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT SIGNATURE |
| Novalloy-X X72S2 (Type W) | Daicel Polymer Ltd. | PC+Styrenic | Novalloy-X |
| Iupilon® LCH2410 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| SABIC® HDPE B5403 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |