Retpol® 9015 HSY
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 70zFsV_Retpol-9015-HSY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Retpol 9015 HSY is a high flow, flame retardant polypropylene homopolymer compound. It has been developed to meet the requirements of the UL 94 V0 rating and the ASNZS 60695.2.12 960°C glow wire rating, whilst providing moderate impact strength and good rigidity. The flame retardant system is based on halogenated hydrocarbon compounds with an antimony trioxide synergist. It is a highly heat stabilized compound. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 20 | J/m | ASTM D256 |
| Unnotched Izod Impact | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 88.0 | °C | ASTM D648 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 180 to 225 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-1200/40 | Techmer Engineered Solutions | ABS | TES |
| Zhongfa PP GR-20H | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Nypol® PA A3 G30 VRM0069 NR312 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Celazole® (T Series) TF-60C | PBI Performance Products, Inc. | PBI | Celazole® (T Series) |
| POLYFORT® FPP 1606U | A. Schulman Inc. | PP, Unspecified | POLYFORT® |