IROGRAN® A 91 P 4945
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 70whKo_IROGRAN-A-91-P-4945.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 91 P 4945 is a polyether based thermoplastic polyurethane intended for injection moulding and extrusion applications. IROGRAN A 91 P 4945 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with high extrudability. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | |||
| -- | 1.14 | g/cm³ | ASTM D792 |
| -- | 1.13 | g/cm³ | DIN 53479 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 55.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 92 | ||
| Shore D, Injection Molded | 39 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 30 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 8.96 | MPa | ASTM D412 |
| 100% Strain | 9.10 | MPa | DIN 53504 |
| 300% Strain | 14.1 | MPa | ASTM D412 |
| 300% Strain | 15.9 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break | 33.6 | MPa | ASTM D412 |
| Break | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 5 | |||
| Break | 670 | % | ASTM D412 |
| Break | 600 | % | DIN 53504 |
| Tear Strength 6 | |||
| -- | 116 | kN/m | ASTM D624 |
| -- | 74 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Hopper Temperature | 25.0 to 35.0 | °C | |
| Rear Temperature | 185 to 195 | °C | |
| Middle Temperature | 185 to 195 | °C | |
| Front Temperature | 185 to 195 | °C | |
| Nozzle Temperature | 185 to 200 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 185 to 195 | °C | |
| Cylinder Zone 2 Temp. | 185 to 195 | °C | |
| Cylinder Zone 3 Temp. | 185 to 195 | °C | |
| Cylinder Zone 4 Temp. | 185 to 195 | °C | |
| Cylinder Zone 5 Temp. | 185 to 195 | °C | |
| Adapter Temperature | 190 to 200 | °C | |
| Die Temperature | 190 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PN300G4 | Polyram Ram-On Industries | PPE+PS | RAMLLOY |
| TIPPLEN® K 793 | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| CALP 3500G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Hanwha Total PE 620L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| Iupiace® EHM103R | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |