ASTATAL™ FV30
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTATAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 70i4Li_ASTATAL-FV30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTATAL™ FV30 is an antistatic low viscosity (high melt flow) grade in the ASTATAL™ range and is well suited for extremely intricate or "difficult to fill" injection moulding applications also requiring antistatic properties. Typical antistatic applications include VTR/audio spool reels and guides, calculator keypads, automotive interior speaker grilles and speedometer gearing. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTATAL™ FV30W ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 31 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 61.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2840 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 90.2 | MPa | ASTM D790 |
| Shear Strength (2.00 mm) | 54.9 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 54 | J/m | ASTM D256 |
| Tensile Impact Strength (1.60 mm) | 98.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 158 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | |
| Melting Temperature | 165 | °C | DSC |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 165 to 185 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 185 to 205 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V738 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Unichem 8715L-30 | Colorite Polymers | PVC, Unspecified | Unichem |
| Fibrolon® P 7550 | FKuR Kunststoff GmbH | Polyolefin, Unspecified | Fibrolon® |
| Geon™ Specialty Suspension Atlas E 46 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |
| Lupolen 4261 A Q 135 | LyondellBasell Industries | HDPE, HMW | Lupolen |