LNP™ STAT-KON™ EX12406C compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 705Xqy_LNP-STAT-KON-EX12406C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON EX12406C is a compound based on Polyetherimide resin containing Electrically Conductive Fillers. Also known as: LNP* STAT-KON* Compound EX12406C Product reorder name: EX12406C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3510 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 3580 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 154 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 470 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 192 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -30 to 150°C | 3.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -30 to 150°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+8 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 370 - 400 | °C | |
| Middle Temperature | 370 - 400 | °C | |
| Front Temperature | 370 - 400 | °C | |
| Mold Temperature | 150 - 165 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 40 - 70 mm/s |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Skyrol® SL30U | SKC Inc. | PET | Skyrol® |
| ENSOFT SM-141-45A | ENPLAST, a Ravago Group Company | SEBS | ENSOFT |
| Karina WHITE PVC COMPOUND -E 855-10/150-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| COPYLENE® CM010G | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| Kepital® TC3020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |