ULTEM™ CRS5011R resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6zshGM_ULTEMCRS5011Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. Resin is RoHS compliant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.40 - 0.70 | % | Internal method |
| Flow : 3.20mm | 0.40 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2900 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 100 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2/5 |
| Fracture 4 | 75.0 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 8.0 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2/5 |
| Fracture 6 | 60 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 3100 | MPa | ASTM D790 |
| -- 8 | 2900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 110 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| -30°C 12 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2100 | J/m | ASTM D4812 |
| -30°C 14 | No Break | ISO 180/1U | |
| 23°C 15 | No Break | ISO 180/1U | |
| Reverse Notch Izod Impact (3.20 mm) | 2100 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 213 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 216 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 16 | 210 | °C | ISO 75-2/Be |
| 0.45 MPa, unannealed, 64.0mm span 17 | 208 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 201 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 204 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 18 | 200 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 19 | 198 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 227 | °C | ASTM D1525 20 |
| -- | 220 | °C | ISO 306/A50 |
| -- | 215 | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 150°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 150°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.31 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 3.20 mm, in Oil | 18 | kV/mm | ASTM D149 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.20 | ASTM D150 | |
| 60 Hz | 3.20 | ASTM D150 | |
| Dissipation Factor | ASTM D150, IEC 60250 | ||
| 50 Hz | 2.1E-3 | ASTM D150, IEC 60250 | |
| 60 Hz | 2.1E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 150 | V | IEC 60112 |
| Solution B | 100 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 343 - 366 | °C | |
| Middle Temperature | 354 - 377 | °C | |
| Front Temperature | 366 - 388 | °C | |
| Nozzle Temperature | 360 - 382 | °C | |
| Processing (Melt) Temp | 366 - 388 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 120*10*4 mm |
| 17 . | 80*10*4 mm |
| 18 . | 120*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPOA10400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| BP RPPC 2008 C BLK | Buckeye Polymers, Inc. | PP Copolymer | BP |
| DURACON® NW-02LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
| DynaMix™ PD1804-BLK | Polymer Dynamix | Acetal (POM) Copolymer | DynaMix™ |
| POTICON RT8 | Otsuka Chemical Co., Ltd. | PPS | POTICON |