Indothene HD 45GP004
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | Indothene HD |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ypWr3_Indothene-HD-45GP004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Indothene-HD 45GP004 is a natural coloured PE 80 (MRS 8 MPa*) material for pipe extrusion, produced by Stirred Tank Heavy Diluent (STHD) Slurry process. It possesses bimodal molecular weight distribution, which improves processability. This grade meets the MFI, Density & Hydrostatic strength requirements of material grade PE 80 as per IS:4984:1995 on "High Density Polyethylene pipe for water supply-specification". The designation of the natural resin of 45GP004 is PE-ENA-C45-T006 as per IS:7328-1992 and shall meet the same given in the amendment No. 2 of IS:4984:1995. When incorporated with adequate quantity of carbon black as specified in clause 5.2.3 of IS:4984:1995, will meet the requirements of the designation PE-EW-C45-T006 mentioned in the clause 5.2 of IS:4984:1995. This grade meets the requirements of Indian Standard IS-10146-1982 on "Polyethylene for its safe use in contact with food stuffs, pharmaceuticals and drinking water". It also conforms to the positive list of constituents as approved in IS:10141:1982. The grade complies with FDA regulation : CFR title 21 , 177.1520, Olefin polymer. The level of antioxidant in 45GP004 is not more than 0.3% by mass of the resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 12 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.45 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (Injection Molded, F50) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 600 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm, Injection Molded) | 800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm, Injection Molded) | No Break | ASTM D256 |
| Additional Information |
|---|
| Hydrostatic Pressure Test, ISO 1167, 9 MPa, 20°C: >100 hrsHydrostatic Pressure Test, ISO 1167, 4.6 MPa, 80°C: >165 hrsHydrostatic Pressure Test, ISO 1167, 4 MPa, 80°C: >1000 hrsMRS, ISO TR9080: >8.0 MPaSCG, ISO 13479: >165 hrsRCP, ISO 13477: >12 barTensile Elongation at Break, ASTM D 638, Type IV, 3.2 mm: >600% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 230 | °C | |
| Die Temperature | 225 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 4 |
| 3 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 55N5006 | The Matrixx Group, Inc. | PC | Matrixx |
| TOLEN H034 FF | SIBUR, LLC | PP Homopolymer | TOLEN |
| EMERGE™ PC 8210-15 | Trinseo | PC | EMERGE™ |
| Ketjenflex® 12 | Axcentive SARL | Plasticizer | Ketjenflex® |
| Sarlink® TPE EE-2280N NAT | Teknor Apex Company | TPE | Sarlink® TPE |