Generic Acetal (POM) Copolymer - Mineral
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6yhiYl_Generic-Acetal-POM-Copolymer---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.44 - 1.60 | g/cm³ | ASTM D792 |
| 23°C | 1.48 - 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.5 - 1.9 | % | ASTM D955 |
| 23°C | 1.2 - 1.9 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 79 - 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 - 8800 | MPa | ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 44.1 - 85.0 | MPa | ASTM D638 |
| Tensile Strain (Yield, 23°C) | 3.5 - 8.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2800 - 7900 | MPa | ASTM D790 |
| 23°C | 2700 - 8500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 68.9 - 188 | MPa | ASTM D790 |
| 23°C | 72.0 - 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.4 - 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 40 - 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 - 163 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 92.2 - 145 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 109 - 146 | °C | ISO 75-2/A |
| Melting Temperature | |||
| -- | 166 | °C | |
| -- | 165 - 167 | °C | ISO 11357-3 |
| CLTE - Flow | 6.0E-5 - 8.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 9.8E+15 - 1.0E+16 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.8 - 121 | °C | |
| Drying Time | 3.0 - 3.1 | hr | |
| Rear Temperature | 175 - 205 | °C | |
| Middle Temperature | 185 - 205 | °C | |
| Front Temperature | 185 - 210 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 190 - 201 | °C | |
| Mold Temperature | 70.0 - 100 | °C | |
| Injection Pressure | 73.5 - 93.8 | MPa | |
| Back Pressure | 0.250 - 3.43 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNPRENE® FF65EC | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| Eltex® PF1315AA | INEOS Olefins & Polymers Europe | MDPE | Eltex® |
| INEOS PP 100-GB06 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| ISOPAK® 540 | Great Eastern Resins Industrial Co Ltd (GRECO) | ABS | ISOPAK® |
| LIHAN® A703 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |