POLYNIL® P85
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6yf9pz_POLYNIL-P85.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® P85 is an unreiforced Polyamide 66 (Nylon 66) for film casting. This 3.3 viscosity Polyamide 66 resin is FDA compliant. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 82.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 85 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 72.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 240 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass | ||
| Melting Temperature | 258 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 750 | °C | |
| 3.20 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | |
| 3.20 mm | 750 | °C | |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G70E-M | TSRC Corporation | SEBS | T-Blend® |
| WELLAMID Nylon 6600 GV 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| ANYPOL SE-2500P | SH Energy & Chemical | PS (EPS) | ANYPOL |
| KOPELEN JM-380UN | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| MAJORIS DG324X - 8229 | AD majoris | PP, Unspecified | MAJORIS |