Stanyl® TW363
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6yOW8k_Stanyl-TW363.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW363 is a Polyamide 46 (Nylon 46) material. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TW363 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.0 | -- | % | |
| Flow | 2.0 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 1850 | 600 | MPa | |
| 120°C | 400 | -- | MPa | |
| 160°C | 350 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield | 60.0 | 45.0 | MPa | |
| Yield, 120°C | 35.0 | -- | MPa | |
| Yield, 160°C | 30.0 | -- | MPa | |
| Nominal Tensile Strain at Break | ISO 527-2 | |||
| -- | > 50 | > 50 | % | |
| 120°C | > 50 | -- | % | |
| 160°C | > 50 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 1800 | 550 | MPa | |
| 120°C | 400 | -- | MPa | |
| 160°C | 350 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 26 | 30 | kJ/m² | |
| 23°C | 75 | 130 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 40 | 40 | kJ/m² | |
| 23°C | 80 | 130 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Transverse | 2.0E-5 | -- | cm/cm/°C | |
| Thermal Index - 5000 hrs | 135 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+9 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 15 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 475 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PI210 | Polymics, Ltd. | API | Pyramid™ |
| SILVER® FG01 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Rigid | SILVER® |
| Geon™ Vinyl Flexible R263AM | PolyOne Corporation | PVC+NBR | Geon™ Vinyl Flexible |
| POLIMAXX 121PC | IRPC Public Company Limited | SAN | POLIMAXX |
| ESTOPLAST EP 1500GY164 | Ester Industries Ltd. | PBT | ESTOPLAST EP |