Modified Plastics MN 6/6-FG 40
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Modified Plastics, Inc. |
| Trademark: | Modified Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6y3H0x_Modified-Plastics-MN-6-6-FG-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified Plastics MN 6/6-FG 40 is a Polyamide 66 (Nylon 66) product filled with 40% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.70 | % | |
| Saturation | 3.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 217 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 11400 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 283 | MPa | ASTM D790 |
| Compressive Strength | 165 | MPa | ASTM D695 |
| Shear Strength | 82.7 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 6.35 mm) | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 260 | °C | |
| 1.8 MPa, Unannealed | 254 | °C | |
| CLTE - Flow | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.30 | ||
| 1 kHz | 3.85 | ||
| 1 MHz | 0.00800 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 0.012 | ||
| 1 kHz | 0.015 | ||
| 1 MHz | 0.019 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Processing (Melt) Temp | 282 | °C | |
| Mold Temperature | 93.3 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-008 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| TECHNYL® C 218L V30 BLACK Z/4 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| THERMOLAST® K TP6CDB (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TPUCO® TPUE-UE90 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| OTECH PVC OM9325-Molding | OTECH Corporation | PVC, Unspecified | OTECH PVC |