ARLEN™ AE4200
| Category: | Nylon 6T , Polyamide 6T |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | ARLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xZVDN_ARLENAE4200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARLEN™AE4200 is a polyamide 6T (nylon 6T) material,. This product is available in North America,. ARLEN™The main characteristics of AE4200 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.10 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00mm | 0.90 | -- | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.90 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.40 | -- | % | ASTM D570 |
| 100°C, 24 hr | 2.6 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 65 | -- | ASTM D785 | |
| Class r | -- | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (2.00 mm) | 80.0 | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 2.00 mm) | 50 | 50 | % | ASTM D638 |
| Flexural Modulus | 2400 | 2200 | MPa | ASTM D790 |
| Flexural Strength | 110 | 100 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 200 | 220 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 135 | -- | °C | ASTM D648 |
| Glass Transition Temperature | 125 | -- | °C | DSC |
| Melting Temperature | 320 | -- | °C | |
| Linear thermal expansion coefficient | ASTM D696 | |||
| Flow | 8.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Lateral | 8.2E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | -- | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | -- | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.018 | -- | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Hopper Temperature | 50 - 90 | °C | |
| Rear Temperature | 315 - 330 | °C | |
| Middle Temperature | 320 - 335 | °C | |
| Front Temperature | 325 - 340 | °C | |
| Nozzle Temperature | 325 - 340 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 150 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Medium Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang W-8205N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| ASTALON™ S3000 | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Infino XI-2008F | SAMSUNG SDI CO., LTD. | PPS+PPA | Infino |
| Karina BLACK PVC COMPOUND 651-48/1-B-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PolyBlend™ 1100 60A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |