Ultramid® A3WG10 CR BK00564
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xW1ZY_UltramidA3WG10CRBK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3WG10 CR BK00564 is a 50% glass fiber reinforced crash resistance and heat aging resistance injection molding PA66 grade. Applications Typical applications include industrial articles having very high rigidity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 17100 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 234 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 14900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 362 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 88 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 257 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 - 305 | °C | |
| Mold Temperature | 80 - 90 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GBF 3020 K1697 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| RONFALIN® RT51 | A. Schulman Europe | ABS | RONFALIN® |
| Clariant Nylon 6/6 6601-L BK-09 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LNP™ THERMOCOMP™ QC008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| Sylvin 83003-73 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |