LNP™ THERMOCOMP™ DC0049XF compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xFGXK_LNP-THERMOCOMP-DC0049XF-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DC0049XF is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DC-1004 FR Product reorder name: DC0049XF |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.31 | g/cm³ | |
| -- | 1.30 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.030 to 0.050 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12600 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 132 | MPa | ASTM D638 |
| Yield | 133 | MPa | ISO 527-2/5 |
| Break 3 | 132 | MPa | ASTM D638 |
| Break | 133 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.1 | % | ASTM D638 |
| Yield | 1.6 | % | ISO 527-2/5 |
| Break 5 | 2.1 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 11100 | MPa | ASTM D790 |
| -- 7 | 10500 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 202 | MPa | |
| Break, 50.0 mm Span | 202 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 58 | J/m | ASTM D256 |
| 23°C 9 | 5.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 10 | 26 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 1.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 139 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.0E-6 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergadur™ PB40 G45 BK006 | PolyOne Corporation | PBT | Bergadur™ |
| APEX® 80128-Y | Teknor Apex Company | PVC, Flexible | APEX® |
| Plastiglas Sensacryl® Ultra | Plastiglas de Mexico S.A de C.V. | Acrylic, Unspecified | Plastiglas |
| TechnoMid PA6 S KSZ | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| Sylvin 9067-95LMW Grey 9368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |