| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Wuxi Kangxi Plastics Technology Co.,Ltd. |
| Trademark: | Kangxi® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xCsp9_KangxiPCABSHI50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kangxi®PC/ABSHI-50 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in the Asia-Pacific region. Kangxi®PC/ABSHI-50 applications include the automotive industry and tools. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 55 | % | ASTM D638 |
| Flexural Modulus 4 | 2200 | MPa | ASTM D790 |
| Flexural Strength 5 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 120 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 100 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weather Resistance - 24 hr (23°C) | 0.10 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME POLYPROPYLENE 10% TALC V2 | RIALTI Srl | PP Homopolymer | RIALFLAME |
| Royalstat R635 | Spartech Plastics | ABS | Royalstat |
| SLOVASTER® B GF 30 FRK 3 | Plastcom | PBT | SLOVASTER® |
| Karina BLACK PVC COMPOUND -E CAK 65-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Paracril® ALT | INSA | NBR | Paracril® |