PPR HDPE02
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xA14W_PPR-HDPE02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Density Polyethylene 8 Melt .950 Density Black Reprocessed |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus - Tangent | 828 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 68.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 77.0 - 82.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 188 - 232 | °C | |
| Middle Temperature | 188 - 232 | °C | |
| Front Temperature | 182 - 227 | °C | |
| Nozzle Temperature | 193 - 232 | °C | |
| Processing (Melt) Temp | 193 - 232 | °C | |
| Mold Temperature | 16.0 - 49.0 | °C | |
| Injection Pressure | 3.00 - 41.0 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 3.00 - 34.0 | MPa | |
| Back Pressure | 0.00 - 1.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: ModerateDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic PFA 6505TZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| ACCUTECH™ CP0437W10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| FORMULA P ELAN 6220 M2 Z | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| POLYFLON™ F-104U | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| Sumiliteresin® PR-50869 I | SBHPP | Phenolic | Sumiliteresin® |