QR Resin QR-1000-GFR10
| Category: | PC , Polycarbonate |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6x7Htt_QR-Resin-QR-1000-GFR10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Available with UV (V) or Release (R). Flame Packages Available (0.0625 in min. thickness): 94V-2, 94V-0, 94-5VA |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 64.8 | MPa | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 143 | °C | |
| 1.8 MPa, Unannealed | 141 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Rear Temperature | 282 to 310 | °C | |
| Middle Temperature | 293 to 316 | °C | |
| Front Temperature | 304 to 327 | °C | |
| Nozzle Temperature | 304 to 321 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT3080-81 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Tarnamid® T-27 GF 40 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| WanBlend® WHT-THF9465T2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Unichem 6742A | Colorite Polymers | PVC, Unspecified | Unichem |
| ELEVATE™ EM518 | Westlake Chemical Corporation | EVA | ELEVATE™ |