INEOS LDPE M21G864
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6w5DCZ_INEOS-LDPE-M21G864.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
M21G864 are particularly suitable for mono and co-extrusion applications such as deep freeze, form fill seal film in general and thin bags. In blends and co-extrusions, they can be used to boost the impact strength of LLDPE, LDPE and recycled polyethylene. M21G864 are ionomers, produced by neutralisation of an ethylene - methacrylic acid copolymer. M21G864 contains slip and antiblock. They offer the following properties:
M21G864 offers high slip film with easy opening properties when used pure in the thickness range 35-80 µm, but slip development takes longer than for standard homopolymer LDPE. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS technical representative for further advice on the use of M21G864. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/0.325 kg) | 0.95 | g/10 min | ISO 1133 |
| Methacrylic Acid Content | 1.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | < 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% Secant, MD : 50 µm, Blown Film | 165 | MPa | |
| 1% Secant, TD : 50 µm, Blown Film | 175 | MPa | |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 50 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 50 µm, Blown Film | 11.0 | MPa | |
| MD : 50 µm, Blown Film | 22.0 | MPa | |
| TD : 50 µm, Blown Film | 21.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 50 µm, Blown Film | 350 | % | |
| TD : Break, 50 µm, Blown Film | 500 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 500 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 540200A45 | SO.F.TER. SPA | SBS | Sofprene T® |
| WELLAMID Nylon 6000 GV 35 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Nypol® PA B3 HL AML0308 NT359 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Elastollan® 695 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Huaxia Shenzhou FKM DS2601-1 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |