LNP™ LUBRICOMP™ LL004 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6uuH8I_LNPLUBRICOMPLL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound LL-4040 Product reorder name: LL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.3 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.9 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2900 | MPa | ASTM D638 |
| -- | 3070 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 74.8 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2 |
| Fracture | 69.6 | MPa | ASTM D638 |
| Fracture | 69.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.8 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2 |
| Fracture | 23 | % | ASTM D638 |
| Fracture | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2960 | MPa | ASTM D790 |
| -- | 3320 | MPa | ISO 178 |
| Flexural Strength | 118 | MPa | ASTM D790, ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.52 | ASTM D3702 Modified | |
| With Self-Static | 0.43 | ASTM D3702 Modified | |
| Wear Factor - Washer | 128 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 91 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.80 | J | ASTM D3763 |
| -- | 1.35 | J | ISO 6603-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 - 360 | °C | |
| Middle Temperature | 366 - 377 | °C | |
| Front Temperature | 382 - 393 | °C | |
| Processing (Melt) Temp | 382 - 388 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 HS SI | RTP Company | Nylon 66 | RTP |
| ESTAPROP H 1080 T6 TD | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| Hanwha Total PE R901U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| HiFill® PA6/6 GF33 HR L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| K-Prene D A-50 | Technovinyl Polymers India Ltd. | MPR | K-Prene |