Generic Nylon 46
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6uRkSu_Generic-Nylon-46.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 46 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 - 1.36 | g/cm³ | ASTM D792 |
| 23°C | 1.18 - 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.5 - 1.8 | % | ASTM D955 |
| 23°C | 1.2 - 2.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.0 - 1.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 960 - 12100 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 54.6 - 100 | MPa | ISO 527-2 |
| Fracture, 23°C | 37.9 - 214 | MPa | ASTM D638 |
| Fracture, 23°C | 53.0 - 170 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.5 - 25 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 9.5 | % | ASTM D638 |
| Fracture, 23°C | 0.60 - 8.1 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 39 - 50 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2210 - 5740 | MPa | ASTM D790 |
| 23°C | 886 - 11300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 62.1 - 352 | MPa | ASTM D790 |
| 23°C | 89.0 - 125 | MPa | ISO 178 |
| Coefficient of Friction | 0.060 - 0.32 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.9 - 36 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 39 - 110 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 78 - 150 | J/m | ASTM D256 |
| 23°C | 5.1 - 36 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 158 - 192 | °C | ISO 75-2/A |
| Continuous Use Temperature | 150 - 151 | °C | ASTM D794 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.3E-5 - 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.0E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.30 - 14 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+6 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 15 - 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 5.40 | IEC 60250 | |
| Comparative Tracking Index | 394 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 80.6 | °C | |
| Drying Time | 4.5 - 7.5 | hr | |
| Suggested Max Moisture | 0.050 - 0.053 | % | |
| Rear Temperature | 300 | °C | |
| Middle Temperature | 310 | °C | |
| Front Temperature | 310 | °C | |
| Nozzle Temperature | 290 - 305 | °C | |
| Processing (Melt) Temp | 310 - 313 | °C | |
| Mold Temperature | 99.8 - 130 | °C | |
| Back Pressure | 5.85 - 6.00 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 46This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1085 | RTP Company | PBT | RTP |
| Small Boss STPR003 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | SBS | Small Boss |
| Clariant Nylon 6 60G13-L | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| EVERLON® TSO-80 | Ever Polymer Co., Ltd. | SEBS+EPDM | EVERLON® |
| Sylvin 9080-55 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |