Generic Polyolefin, Unspecified
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6uGs3u_Generic-Polyolefin-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyolefin, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.890 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 0.870 - 1.51 | g/cm³ | ISO 1183 |
| -- | 0.890 - 1.42 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.51 - 0.56 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.30 - 30 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.50 - 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.56 - 1.5 | % | ASTM D955 |
| Transverse flow : 23°C | 1.2 - 1.8 | % | ASTM D955 |
| 23°C | 0.20 - 1.2 | % | ISO 294-4 |
| Carbon Black Content | 34 - 40 | % | ASTM D1603 |
| Moisture Content | 938 - 2063 | ppm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 20 - 120 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 28 - 96 | ASTM D2240 | |
| 23°C | 29 - 97 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1430 - 2510 | MPa | ASTM D638 |
| 23°C | 4.50 - 2560 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 8.60 - 26.2 | MPa | ASTM D638 |
| Yield, 23°C | 3.92 - 53.8 | MPa | ISO 527-2 |
| Fracture, 23°C | 6.00 - 17.3 | MPa | ASTM D638 |
| Fracture, 23°C | 10.6 - 13.9 | MPa | ISO 527-2 |
| 23°C | 1.31 - 61.9 | MPa | ASTM D638 |
| 23°C | 10.0 - 19.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 17 | % | ASTM D638 |
| Yield, 23°C | 4.4 - 40 | % | ISO 527-2 |
| Fracture, 23°C | 4.0 - 510 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 800 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6.89 - 2490 | MPa | ASTM D790 |
| 23°C | 20.0 - 2180 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 20.0 - 95.1 | MPa | ASTM D790 |
| 23°C | 58.2 - 105 | MPa | ISO 178 |
| Yield, 23°C | 16.0 - 99.7 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 47 - 53 | µm | |
| secant modulus | |||
| MD | 70.1 - 426 | MPa | ASTM D882 |
| TD | 96.9 - 426 | MPa | ASTM D882 |
| 23°C | 90.0 - 344 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Yield | 8.96 - 18.6 | MPa | ASTM D882 |
| TD : Yield | 7.79 - 15.4 | MPa | ASTM D882 |
| Yield, 23°C | 13.7 - 15.1 | MPa | ISO 527-3 |
| MD : Fracture | 20.5 - 33.1 | MPa | ASTM D882 |
| TD : Fracture | 11.3 - 48.0 | MPa | ASTM D882 |
| Fracture, 23°C | 24.5 - 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| Yield, 23°C | 12 - 40 | % | ISO 527-3 |
| MD : Fracture | 190 - 680 | % | ASTM D882 |
| TD : Fracture | 480 - 870 | % | ASTM D882 |
| Fracture, 23°C | 800 - 900 | % | ISO 527-3 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 20 - 3000 | g | ASTM D1922 |
| TD | 80 - 1100 | g | ASTM D1922 |
| Seal Initiation Temperature | 104 - 115 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 7.00 - 67.4 | kN/m | ASTM D624 |
| Compression Set | 15 - 75 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 - 55 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 11 - 820 | J/m | ASTM D256 |
| 23°C | 8.3 - 60 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 2.30 - 10.3 | kJ/m² | ASTM D256 |
| Dart Drop Impact (23°C) | 20.2 - 22.8 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 61.0 - 144 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 35.0 - 108 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 46.1 - 124 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 49.3 - 55.1 | °C | ISO 75-2/A |
| Brittleness Temperature | -75.0 - -8.00 | °C | ASTM D746 |
| Glass Transition Temperature | 84.0 - 140 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 40.0 - 108 | °C | ASTM D1525 |
| -- | 46.5 - 131 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 163 - 216 | °C | |
| -- | 75.8 - 128 | °C | DSC |
| -- | 131 - 143 | °C | ISO 11357-3 |
| -- | 105 - 145 | °C | ASTM D3418 |
| CLTE - Flow | |||
| -- | 6.0E-5 - 7.0E-5 | cm/cm/°C | ASTM D696 |
| -- | 7.0E-5 - 7.1E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (23°C) | 0.18 - 0.23 | W/m/K | ISO 8302 |
| RTI Elec | 65.0 - 106 | °C | UL 746 |
| RTI Imp | 65.0 - 106 | °C | UL 746 |
| RTI | 65.0 - 106 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.0E+2 - 1.1E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+2 - 2.5E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 40 - 70 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 2.27 - 3.38 | ASTM D150 | |
| 23°C | 2.30 - 2.40 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 1.0E-4 - 1.3E-3 | ASTM D150 | |
| 23°C | 2.0E-4 - 3.5E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | |||
| -- | 26 - 41 | % | ASTM D2863 |
| -- | 33 - 40 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 4 - 93 | ASTM D2457 | |
| Refractive Index | 1.525 - 1.530 | ASTM D542 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.20 - 2.6 | % | ASTM D1003 |
| Chemical Resistance | Nominal Value | Unit | Test Method |
|---|---|---|---|
| HCl solution impregnation test | % | IEC 60811 | |
| NaOH solution impregnation test | % | IEC 60811 | |
| Oxalic acid impregnation test | % | IEC 60811 | |
| Hydrocarbon Impregnation Test | % | IEC 60811 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 4.7 - 6.2 | min | |
| Thermoset Mix Viscosity | 40.0 - 1000 | cP | ASTM D2393 |
| Demold Time | 37 - 180 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.5 - 105 | °C | |
| Drying Time | 1.5 - 8.0 | hr | |
| Hopper Temperature | 95.0 - 145 | °C | |
| Rear Temperature | 150 - 280 | °C | |
| Middle Temperature | 155 - 280 | °C | |
| Front Temperature | 160 - 280 | °C | |
| Nozzle Temperature | 210 - 271 | °C | |
| Processing (Melt) Temp | 188 - 195 | °C | |
| Mold Temperature | 25.0 - 40.5 | °C | |
| Injection Pressure | 6.55 - 98.0 | MPa | |
| Holding Pressure | 5.17 - 113 | MPa | |
| Back Pressure | 0.689 - 12.5 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyolefin, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 55.0 - 110 | °C | |
| Drying Time | 2.0 - 3.5 | hr | |
| Cylinder Zone 1 Temp. | 96.6 - 183 | °C | |
| Cylinder Zone 2 Temp. | 98.0 - 193 | °C | |
| Cylinder Zone 3 Temp. | 80.0 - 193 | °C | |
| Cylinder Zone 4 Temp. | 149 - 192 | °C | |
| Cylinder Zone 5 Temp. | 109 - 206 | °C | |
| Adapter Temperature | 116 - 196 | °C | |
| Melt Temperature | 163 - 167 | °C | |
| Die Temperature | 157 - 218 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyolefin, UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NM15-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Advanced Composites ATX904-20 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Colorite Rigid PVC 2600 UVLCR | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| KOPLA PA66 KDT1040 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Hostacom TKC 218N | LyondellBasell Industries | PP Copolymer | Hostacom |