ACCUTECH™ HP0339C10L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6tNtBD_ACCUTECH-HP0339C10L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0339C10L is a polypropylene homopolymer (PP Homopoly) product, and its filler is 10% calcium carbonate filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.959 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 33.0 | MPa | ASTM D638 |
| Fracture | 17.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 120 | % | ASTM D638 |
| Flexural Modulus | 1400 | MPa | ASTM D790 |
| Flexural Strength | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 102 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 58.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 1002C | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Vi-Chem PVC 80 Durometer Black | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| LNP™ THERMOCOMP™ 9X06482 compound | SABIC Innovative Plastics | Nylon 46 | LNP™ THERMOCOMP™ |
| Styropek® BFL 397 | Styropek S.A. de C.V. | PS (EPS) | Styropek® |
| LNP™ THERMOCOMP™ OF008E compound | SABIC Innovative Plastics | PPS | LNP™ THERMOCOMP™ |