MAJ'ECO PSCP300W - 3737
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6sckIb_MAJ-ECO-PSCP300W---3737.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO PSCP300W - 3737 is a 30% wood fibre reinforced polystyrene compound intended for injection moulding. MAJ'ECO PSCP300W - 3737 has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage (2.00 mm) | 0.10 - 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3870 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 26.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 3770 | MPa | ISO 178 |
| Flexural Stress 2 | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VALOX™ 830F resin | SABIC Innovative Plastics | PBT+PET | VALOX™ |
| MAJORIS DG308X - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| OnFlex™ V 3050D-S0097 | PolyOne Corporation | TPE | OnFlex™ |
| 3M™ Dyneon™ PTFE Compound TF 8390 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| VALOX™ 855 resin | SABIC Innovative Plastics | PBT | VALOX™ |