| Trexlink ™ 4750 is a highly engineered Thermoplastic Elastomer for use in applications requiring integrally colored material. This material is UV stabilized and can be pre-colored in most Automotive Interior or other colors. It can be easily processed by injection molding, blow molding or extrusion. Applications include critical color matched Automotive components such cup holders, mats, seals, soft seat trim. Also works well for two-shot molding or over-mold components such as grips and handles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec, Injection Molded) | 55 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 1.60 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 4.60 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 540 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 18 | kN/m | ISO 34-1 |
| Compression Set 5(70°C, 22 hr) | 28 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6(135°C, 1000 hr) | 10 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7(135°C, 1000 hr) | 17 | % | ISO 188 |
| Change in Shore Hardness in Air (135°C, 1000 hr) | 4.0 | ISO 188 |
| Additional Information |
|---|
| Change in Color, SAE J1885, 1240.8kJ/m² exposure: <3.0 delta EChange in Modulus at 100%, ISO 118, method B, 1000 hrs, 135°C: 21% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 182 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 204 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 188 - 210 | °C | |
| Melt Temperature | 193 - 216 | °C | |
| Die Temperature | 193 - 216 | °C | |
| Take-Off Roll | 21.1 - 48.9 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: general purpose 3 to 1 compression ratio |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| 3 . | Type 1 |
| 4 . | Method B, right-angle specimen (cut) |
| 5 . | Type a |
| 6 . | Method B |
| 7 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNPRENE® FE70DH | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| Axpoly® PP19 1047 | Axion Polymers | PP, Unspecified | Axpoly® |
| EPO-TEK® H31D | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LOTTMER HS-050AB | Lotte Chemical Corporation | TPE | LOTTMER |
| LNP™ THERMOCOMP™ HB006 compound | SABIC Innovative Plastics | Nylon 11 | LNP™ THERMOCOMP™ |