RTP 1399 X 130032 A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6sV1Rt_RTP-1399-X-130032-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermally Conductive - Glass Fiber - Electrically Conductive - EMI/RFI Shielding - (Preliminary Data Sheet) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.050 - 0.15 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19300 | MPa | ASTM D638 |
| Tensile Strength | 159 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | < 1.0 | % | ASTM D638 |
| Flexural Modulus | 17900 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 271 | °C | ASTM D648 |
| Thermal Conductivity | |||
| -- 1 | 0.60 | W/m/K | ASTM E1530 |
| -- 2 | 3.0 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+6 | ohms | ASTM D257 |
| -- | < 1.0E+5 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 307 - 329 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Remove hopper magnets. |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207D Z | RTP Company | Nylon 612 | RTP |
| ULTEM™ UF5011S resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |
| Bapolene® 80 | Bamberger Polymers, Inc. | PET | Bapolene® |
| Alkathene® LD1217 | Qenos Pty Ltd | LLDPE | Alkathene® |
| Globalene® 73F4-3 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |