Cariflex® IR0401 BU
| Category: | IR , Polyisoprene |
| Manufacturer: | Kraton Polymers LLC |
| Trademark: | Cariflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6sLHvo_Cariflex-IR0401-BU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cariflex™ IR0401 BU Latex is a water-based emulsion of an anionically polymerized polyisoprene with a high cis-1,4 content, high molecular weight and a high linearity. The emulsion also contains a non-staining antioxidant (typical level of 0.1% mass on solids) and a surfactant. Cariflex™ IR0401 BU Latex is a synthetic rubber emulsion and can be used as an alternative to natural rubber latex in a variety of applications ranging from dipping to extrusion. It offers specific advantages such as light color, consistency and low levels of impurities. Cariflex™ IR0401 BU Latex is made under Good Manufacturing Practices, but additional requirements may apply to food contact, pharmaceutical and medical device applications using this material. Reference should always be made to the local legislation regulating these applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ISO 2781 |
| 1,4-cis Content | Internal Method | ||
| -- 1 | > 82.0 | wt% | |
| -- 2 | > 90.0 | wt% | |
| Antioxidant Additive | 0.10 | % | Internal Method |
| Ash Content | < 0.10 | % | Internal Method |
| Gel Content | 0.0 | % | |
| Limiting Viscosity Number | 670 to 920 | cm³/g | Internal Method |
| Molecular Weight | 1500000 to 2500000 | g/mol | Internal Method |
| pH | 9.5 to 12.0 | Internal Method | |
| Solids Content | > 63 | % | Internal Method |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Freezing Point | 0 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity | < 150 | mPa·s | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Median Particle Size | < 1.8 | µm | Internal Method |
| Odor | Neutral | ||
| T.A.M.C. at Drumming | < 1000 | CFU/ml | USP 24 |
| Note Message | |
|---|---|
| 1 . | NMR |
| 2 . | FTIR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEDUR® L 9560-3 S | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| ULTEM™ ATX200 resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |
| Exxelor™ VA 1801 | ExxonMobil Chemical | TP, Unspecified | Exxelor™ |
| Later 4-V0 | LATI S.p.A. | PBT | Later |
| MAJORIS PBT 9237 20 FV | AD majoris | PBT | MAJORIS |